Tabel Konversi Alat Ukur Kekerasan Baja Brinnel, Rockwell, Vikers
Tabel Konversi Alat Ukur Kekerasan Baja Brinnel, Rockwell, Vikers
Table Hardness Tester
Apa Itu Kekerasan ( Hardness ) Kekerasan juga didefinisikan sebagai kemampuan suatu material untuk menahan beban identasi atau penetrasi ( penekanan ). Didunia Teknik, Umumnya pengujian kekerasan menggunakan 4 Macam Metode Pengujian kekerasan, Yakni :
- Brinnel (HB / BHN)
- Rockwell (HR / RHN)
- Vikers (HV / VHN)
- Micro Hardness ( Namun jarang sekali dipakai – red)
Kisaran kekerasan untuk baja yang diberi perlakuan panas
Heat Treated Condition |
Q | R | S | T | U | V | W | X | Z |
---|---|---|---|---|---|---|---|---|---|
Tensile Strength |
625-775 n/mm2 | 700-850 n/mm2 | 775-925 n/mm2 | 850-1000 n/mm2 | 925-1075 n/mm2 | 1000-1150 n/mm2 | 1075-1225 n/mm2 |
1150-1300 n/mm2 |
1550 n/mm2 |
Hardness Brinell |
179-229 | 201-225 | 223-277 | 248-302 | 269-331 | 293-352 | 311-375 | 345-401 | 444 |
Tabel Konversi Alat Ukur Kekerasan Baja
Tabel ini menunjukkan perkiraan kekerasan baja menggunakan skala Brinell, Rockwell B dan C dan Vickers. Grafik konversi ini disediakan untuk panduan hanya karena setiap skala menggunakan metode pengukuran kekerasan yang berbeda. Kolom sebelah kanan menunjukkan kekuatan tarik setara dengan perkiraan.
Produk Kategori Hardness TesterReference Table: Steel hardness conversion chart – all values approximate. | ||||
---|---|---|---|---|
Brinell Hardness HB |
Rockwell HRC |
Rockwell HRB |
Vickers HV |
N/mm² |
800 | 72 | |||
780 | 71 | |||
760 | 70 | |||
752 | 69 | |||
745 | 68 | |||
746 | 67 | |||
735 | 66 | |||
711 | 65 | |||
695 | 64 | |||
681 | 63 | |||
658 | 62 | |||
642 | 61 | |||
627 | 60 | |||
613 | 59 | |||
601 | 58 | 746 | ||
592 | 57 | 727 | ||
572 | 56 | 694 | ||
552 | 55 | 649 | ||
534 | 54 | 120 | 589 | |
513 | 53 | 119 | 567 | |
504 | 52 | 118 | 549 | |
486 | 51 | 118 | 531 | |
469 | 50 | 117 | 505 | |
468 | 49 | 117 | 497 | |
456 | 48 | 116 | 490 | 1569 |
445 | 47 | 115 | 474 | 1520 |
430 | 46 | 115 | 458 | 1471 |
419 | 45 | 114 | 448 | 1447 |
415 | 44 | 114 | 438 | 1422 |
402 | 43 | 114 | 424 | 1390 |
388 | 42 | 113 | 406 | 1363 |
375 | 41 | 112 | 393 | 1314 |
373 | 40 | 111 | 388 | 1265 |
360 | 39 | 111 | 376 | 1236 |
348 | 38 | 110 | 361 | 1187 |
341 | 37 | 109 | 351 | 1157 |
331 | 36 | 109 | 342 | 1118 |
322 | 35 | 108 | 332 | 1089 |
314 | 34 | 108 | 320 | 1049 |
308 | 33 | 107 | 311 | 1035 |
300 | 32 | 107 | 303 | 1020 |
290 | 31 | 106 | 292 | 990 |
277 | 30 | 105 | 285 | 971 |
271 | 29 | 104 | 277 | 941 |
264 | 28 | 103 | 271 | 892 |
262 | 27 | 103 | 262 | 880 |
255 | 26 | 102 | 258 | 870 |
250 | 25 | 101 | 255 | 853 |
245 | 24 | 100 | 252 | 838 |
240 | 23 | 100 | 247 | 824 |
233 | 22 | 99 | 241 | 794 |
229 | 21 | 98 | 235 | 775 |
223 | 20 | 97 | 227 | 755 |
216 | 19 | 96 | 222 | 716 |
212 | 18 | 95 | 218 | 706 |
208 | 17 | 95 | 210 | 696 |
203 | 16 | 94 | 201 | 680 |
199 | 15 | 93 | 199 | 667 |
191 | 14 | 92 | 197 | 657 |
190 | 13 | 92 | 186 | 648 |
186 | 12 | 91 | 184 | 637 |
183 | 11 | 90 | 183 | 617 |
180 | 10 | 89 | 180 | 608 |
175 | 9 | 88 | 178 | 685 |
170 | 7 | 87 | 175 | 559 |
167 | 6 | 86 | 172 | 555 |
166 | 5 | 86 | 168 | 549 |
163 | 4 | 85 | 162 | 539 |
160 | 3 | 84 | 160 | 535 |
156 | 2 | 83 | 158 | 530 |
154 | 1 | 82 | 152 | 515 |
149 | 81 | 149 | 500 | |
147 | 80 | 147 | 490 | |
143 | 79 | 146 | 482 | |
141 | 78 | 144 | 481 | |
139 | 77 | 142 | 480 | |
137 | 76 | 140 | 475 | |
135 | 75 | 137 | 467 | |
131 | 74 | 134 | 461 | |
127 | 72 | 129 | 451 | |
121 | 70 | 127 | 431 | |
116 | 68 | 124 | 422 | |
114 | 67 | 121 | 412 | |
111 | 66 | 118 | 402 | |
107 | 64 | 115 | 382 | |
105 | 62 | 112 | 378 | |
103 | 61 | 108 | 373 | |
95 | 56 | 104 | ||
90 | 52 | 95 | ||
81 | 41 | 85 | ||
76 | 37 | 80 | ||
Brinell HB |
Rockwell HRC |
Rockwell HRB |
Vickers HV |
N/mm² |
3000kg 10mm Ball |
150kg Brale |
100kg 1/16″ Ball |
Diamond Pyramid 120kg |
Tensile strength (Approx) |
Tabel referensi: Bagan konversi Alat Ukur Kekerasan Baja
Karena berbagai jenis tes kekerasan tidak semuanya mengukur kombinasi yang sama dari sifat material, konversi dari satu skala kekerasan ke yang lain hanya merupakan proses perkiraan. Karena berbagai variasi di antara berbagai bahan, tidak mungkin menyatakan batas keyakinan untuk kesalahan dalam menggunakan bagan konversi. |
Sumber : https://www.steelexpress.co.uk/steel-hardness-conversion.html